Method and Apparatus for Continuously Fabricating a Composite Sandwich Structure

ABSTRACT

A method for continuously fabricating a composite sandwich structure includes the steps of: (1) preheating a laminate to a preforming temperature above a glass transition temperature of the laminate but below or equal to a crystalline melt temperature of the laminate as the laminate is substantially continuously moved through a preheating zone, wherein the laminate comprises a first face sheet, a second face sheet and a core sandwiched between the first face sheet and the second face sheet; (2) consolidating the laminate as the laminate is substantially continuously moved through a consolidation zone in line with the preheating zone to form a continuous length of the composite sandwich structure; (3) moving the composite sandwich structure, substantially continuously, through at least one of a texturing zone and a coating zone; and (4) incrementally applying at least one of a surface texture and a surface coating to at least one surface of the composite sandwich structure.

FIELD

The present disclosure is generally related to composite laminates and,more particularly, to apparatus and methods for continuous manufacturingof composite sandwich structures.

BACKGROUND

Composite materials are widely used for aerospace applications. Whilestructural composites are becoming more prevalent in airframe design,composites have long been used for various components of an aircraft'sinterior, primarily because of the material's light weight and highstrength-to-weight ratio. Aircraft interiors may be less demandingstructurally when compared to airframe parts, but they are still subjectto demanding performance requirements such as mechanical strength,dimensional stability and low heat release in the event of a fire.

The most widely used composite applications for aircraft interiors aresandwich structures, commonly referred to as sandwich panels. Sandwichpanels are made using a thick, lightweight core sandwiched between twothin face sheets (e.g., plies of a fiber-reinforced materialpre-impregnated with a matrix material), which increases the panel'sstiffness with little added weight. Sandwich panels are cost-effectivebecause the core material is less expensive and weighs less than thecomposite face sheets and can be cured or processed with the face sheetsin a single operation. Sandwich panels are commonly used for flooring,ceilings, sidewalls, lavatories, stow bins, cargo hold liners and thelike.

Flat sandwich panels are typically fabricated with flat press moldingconducted at a high temperature and high pressure, in which a coredlaminate is placed in a large press and crushed down to a predeterminedthickness in a process commonly referred to as “crush core.” Crush coreis an efficient and economical process for fabrication of sandwichpanels. One disadvantage to the core crush process is it is anon-continuous process in which individual sandwich panels arefabricated and trimmed. Another disadvantage to the crush core processis the challenge of fabricating sandwich panels within applicabletolerances. Otherwise, a costly and lengthy re-work process may berequired or material waste may result if the damage is so extensive thatit is beyond repair.

Further, many interior parts can include contoured shapes or othernon-planar (e.g., complex) shapes. These contoured shapes are typicallymade from flat sandwich panels by a cut and fold process. In thisprocess, a portion of one face sheet is removed to expose the core.Adhesive is then applied to the exposed core and the sandwich panel isfolded to the desired position and clamped until the adhesive cures.While this process is economical, one disadvantage is the material wasteassociated with the cut and fold and the challenge of consistentfabrication of panels within the applicable tolerances.

Following final inspection of the sandwich panel, desired surfacedecorations are applied to individual sandwich panels. Examples ofdecorative surfaces typically include plastic films or paint. However,painting requires additional surface preparation steps, such as filling,sanding and primer application. A decorative film eliminates some of thesurface-prep and finishing steps, but may add cost and weight to thepart.

Accordingly, those skilled in the art continue with research anddevelopment efforts in the field of composite sandwich panels.

SUMMARY

In one embodiment, the disclosed method for continuously fabricating acomposite sandwich structure includes the steps of: (1) preheating alaminate to a preforming temperature above a glass transitiontemperature of the laminate and below or equal to a crystalline melttemperature of the laminate as the laminate is substantiallycontinuously moved through a preheating zone, wherein the laminatecomprises a first face sheet, a second face sheet and a core sandwichedbetween the first face sheet and the second face sheet; (2)consolidating the laminate as the laminate is substantially continuouslymoved through a consolidation zone in line with the preheating zone toform a continuous length of the composite sandwich structure; (3) movingthe composite sandwich structure, substantially continuously, through atleast one of a texturing zone and a coating zone; and (4) incrementallyapplying at least one of a surface texture and a surface coating to atleast one surface of the composite sandwich structure.

In another embodiment, the disclosed apparatus for continuouslyfabricating a composite sandwich structure includes a preheating deviceto preheat a laminate to a preforming temperature above a glasstransition temperature of the laminate and below or equal to acrystalline melt temperature of the laminate as the laminate is moved,substantially continuously, through the preheating device, wherein thelaminate comprises a first face sheet, a second face sheet and a coresandwiched between the first face sheet and the second face sheet, acontinuous compression molding device to consolidate the laminate as thelaminate is moved, substantially continuously, through the continuouscompression molding device to form a continuous length of the compositesandwich structure, and at least one of a texturing device and a coatingdevice to apply at least one of a surface texture and a surface coatingto at least one surface of the composite sandwich structure, and whereinthe preheating device, the continuous compression molding device and theat least one of the texturing device and the coating device are arrangedin a continuous linked sequence.

In yet another embodiment, the disclosed continuously fabricatedcomposite sandwich structure includes a laminate including a first facesheet, a second face sheet and a core sandwiched between the first facesheet and the second face sheet, and at least one of a surface textureand a surface coating applied to the composite sandwich structure, andwherein the composite sandwich structure is continuously fabricated by:(1) preheating the laminate to a preforming temperature above a glasstransition temperature of the laminate and below or equal to acrystalline melt temperature of the laminate as the laminate issubstantially continuously moved through a preheating zone; (2)consolidating the laminate by heating the laminate to a thermoformingtemperature sufficient to allow a free flow of a polymeric component ofthe laminate and incrementally forming the laminate at the thermoformingtemperature into a desired shape as the laminate is substantiallycontinuously moved through a consolidation zone in line with thepreheating zone to form a continuous length of the composite sandwichstructure; and (3) incrementally applying at least one of the surfacetexture and the surface coating to the at least one surface of thecomposite sandwich structure as the composite sandwich structure issubstantially continuously moved through at least one of a texturingzone and a coating zone in line with the consolidation zone.

Other embodiments of the disclosed apparatus and method will becomeapparent from the following detailed description, the accompanyingdrawings and the appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic fragmentary perspective view of an embodiment ofthe disclosed continuously formed composite sandwich structure ofindeterminate length;

FIG. 2 is a schematic illustration of an embodiment of the disclosedapparatus for continuously fabricating the composite sandwich structure;

FIG. 3 is a schematic illustration of another embodiment of thedisclosed apparatus for continuously fabricating the composite sandwichstructure;

FIG. 4 is an illustration of a temperature profile of the disclosedcontinuously formed composite sandwich structure during a preheating andconsolidation process;

FIG. 5 is an illustration of a temperature profile of the disclosedcontinuously formed composite sandwich structure during a preheating,preforming and consolidation process;

FIG. 6 is a schematic cross-sectional view of an embodiment of tool diesused to form the composite sandwich structure;

FIG. 7 is a schematic cross-sectional view of another embodiment of thetool dies used to form the composite sandwich structure;

FIG. 8 is a schematic cross-sectional view of another embodiment of thetool dies used to form the composite sandwich structure;

FIG. 9 is a schematic illustration of another embodiment of thedisclosed apparatus for continuously fabricating the composite sandwichstructure;

FIG. 10 is a schematic illustration of another embodiment of thedisclosed apparatus for continuously fabricating the composite sandwichstructure;

FIG. 11 is a schematic illustration of another embodiment of thedisclosed apparatus for continuously fabricating the composite sandwichstructure;

FIG. 12 is a schematic illustration of another embodiment of thedisclosed apparatus for continuously fabricating the composite sandwichstructure;

FIG. 13 is a schematic illustration of another embodiment of thedisclosed apparatus for continuously fabricating the composite sandwichstructure;

FIG. 14 is a schematic illustration of another embodiment of thedisclosed apparatus for continuously fabricating the composite sandwichstructure;

FIG. 15 is a flow diagram of an embodiment of the disclosed method forcontinuously fabricating the composite sandwich structure;

FIG. 16 is a schematic illustration of an aircraft; and

FIG. 17 is a schematic block diagram of aircraft production and servicemethodology.

DETAILED DESCRIPTION

The following detailed description refers to the accompanying drawings,which illustrate specific embodiments and/or examples described by thedisclosure. Other embodiments and/or examples having differentstructures and operations do not depart from the scope of the presentdisclosure. Like reference numerals may refer to the same feature,element or component in the different drawings.

Illustrative, non-exhaustive embodiments, which may be, but are notnecessarily, claimed, of the subject matter according the presentdisclosure are provided below.

The present disclosure recognizes and takes into account that processesexist for the fabrication of composite laminates formed from a multipleply stack (a stacked plurality of plies) of fiber-reinforced plasticmaterial. In addition to non-continuous processes such as pressing andautoclave forming, there are continuous processes such as compressionmolding. However, convectional continuous processes (e.g., continuouscompression molding) are not capable of successfully fabricatingcomposite laminates formed from a core sandwiched between two plies offiber-reinforced plastic material (composite sandwich structures). Onereason for this lack of success is due to the fact that the sandwichstructure is too stiff to be formed without cracking the core materialand/or tearing the face sheets under the pressure applied by compressionmolding. Another reason is that the continuous process does not applysufficient heat to the sandwich structure to maintain dimensionalstability of the sandwich structure following thermal forming, whichresults in a springback effect that leads to the sandwich structurehaving an undesirable final shape.

The present disclosure also recognizes and takes into account thatnon-continuous processes exist for the fabrication of compositelaminates formed from a core sandwiched between two plies offiber-reinforced plastic material (composite sandwich structures).However, convectional non-continuous processes (e.g., pressing andautoclave forming) are not capable of producing sandwich structures incontinuous lengths. Moreover, the processes mentioned above are notcapable of producing sandwich structures that have a curvature, forexample, along their length and/or width, or other complex shape.

Embodiments of the apparatuses and methods disclosed herein provide forthe fabrication and forming of composite laminates formed from a coresandwiched between two plies of fiber-reinforced plastic material(composite sandwich structures) using a modified continuous compressionmolding technique or process. As will be described below in more detail,the composite sandwich structures (e.g., laminates and laminate parts)may be fabricated in a continuous process with consistent results thatis, for example, without damage to the core and/or face sheets orspringback. The embodiments disclosed herein may be employed in a widerange of applications, and may be especially suited for formingcomposite sandwich structures used in aircraft applications, which mayinclude, without limitation, flooring, ceilings, sidewalls, lavatories,stow bins, and cargo hold liners. Further, the composite sandwichstructures may be formed to have various cross-sectional shapes.

FIG. 1 is a schematic fragmentary perspective view of an embodiment of acomposite sandwich structure 100 of indeterminate length L. Thecomposite sandwich structure 100, also referred to as a sandwich panel,may be fabricated in continuous lengths according to the disclosedmethod 300 (FIG. 15) using a continuous compression molding (CCM)fabrication apparatus 200 (FIG. 2). Generally, as used here,“continuous” means an elongated material having a length that is ordersof magnitude greater than its width. The composite sandwich structure100 may be either straight, for example, as illustrated in FIG. 1, orhave one or more curvatures along its length.

As an example, the composite sandwich structure 100 may have alongitudinal curvature formed along its length (e.g., approximatelyparallel to its longitudinal axis 102). As another example, thecomposite sandwich structure 100 may have a transverse curvature formedalong its length (e.g., approximately perpendicular to its longitudinalaxis 102). While the composite sandwich structure 100 illustrated inFIG. 1 has a generally rectangular cross section, a variety of othercross-sectional shapes are possible.

In an example construction, the composite sandwich structure 100includes an outer first face sheet, or skin, 104, an outer second facesheet, or skin, 106, and core 108 sandwiched between the first facesheet 104 and the second face sheet 106. While only a single first facesheet 104 and a single second face sheet 106, opposite the first facesheet 104, are illustrated in FIG. 1, in other example constructions,more than one first face sheet 104 and/or more than one second facesheet 106 may be used.

The first face sheet 104 and the second face sheet 106 may typically beplies, sheets or layers of a fiber reinforcing material impregnated(e.g., pre-impregnated) with a polymer matrix material. As an example,the first face sheet 104 and the second face sheet 106 are layers offiber-reinforced polymer prepreg.

The fiber reinforcement may be a woven or nonwoven fabric or tape formedfrom tows of the reinforcing material (e.g., bundles of reinforcingfibers or filaments). As non-limiting examples, the fiber reinforcementmay be carbon fiber, glass fiber (s-type or e-type), aramid fiber andthe like. The fibers within each of the first face sheet 104 and/or thesecond face sheet 106 may be oriented in a unidirectional or non-uniformarrangement, depending upon the particular application.

The polymer matrix material may be a thermoset (thermosetting) resin ora thermoplastic resin. As non-limiting examples, the matrix material maybe an epoxy resin, a phenolic resin and the like.

The core 108 may be formed from any suitable polymer material. Asnon-limiting examples, the core 108 may be thermoplastic, polymeric foamand the like. The core 108 may be a solid structure (e.g., notcontaining substantial spaces or gaps) or a honeycomb structure (e.g.,containing a plurality of cells). Thermoplastic matrix materials mayalso include polyetheretherketone (PEEK), polyetherketoneketone (PEKK),polyphenylsulfone (PPS) and polyetherimide (PEI).

Thus, the composite sandwich structure 100 includes a laminate formedfrom layers of the face sheets 104, 106 and the core 108 in a cured andconsolidated composite form. The polymer matrix material of the firstface sheet 104 and the second face sheet 106 and the polymer material ofthe core 108 may be the same or may be different.

FIG. 2 is a schematic illustration of an embodiment of the disclosed CCMfabrication apparatus, generally referred to herein as the apparatus,200 used to form the composite sandwich structure 100. The apparatus 200broadly includes a material supply zone 202, a preheating zone 204 and aconsolidation zone 206. The apparatus 200 also includes a cutting zone212 and an inspection zone 214.

The apparatus 200 also includes a pulsating drive mechanism 226. Thepulsating drive mechanism 226 is configured to incrementally move alaminate 110 forward through the zones of the apparatus 200 duringfabrication of the composite sandwich structure 100. In lieu of thepulsating drive mechanism 226, other types of mechanisms may be used formoving the laminate 110 along in a similar manner.

Multiple material layers 112 forming the composite sandwich structure100 (e.g., first face sheet 104, second face sheet 106 and core 108) aresupplied (e.g., to the supply zone 202) in continuous form. As anexample, one or more of the material layers 112 may be supplied fromcontinuous rolls (not shown) and are stacked into a laminate at thematerial supply zone 202. As another example, the material layers 112may be supplied in the form of a pre-stacked laminate that is tackedtogether (not shown). Thus, in either example, a stack of the materiallayers 112, or the laminate 110 (e.g., a stacked laminate), exits thesupply zone 202.

A substantially flat laminate 110 (e.g., stack of material layers 112)is introduced, fed or otherwise directed to the preheating zone 204,linearly in the direction of arrow 218. In an example implementation,the material layers 112 are fed to the preheating zone 204 along withsheet members 208 applied to outer surfaces of the laminate 110. As anexample, the sheet members 208 are supplied in continuous form, forexample, from supply rolls 216. The sheet members 208 are configured toprotect the surfaces of the laminate 110 during a preforming operationand/or a forming operation of the composite sandwich structure 100.

For example, the sheet members 208 are located between the outersurfaces of the laminate 110 and tool dies used to partially form orfully form the composite sandwich structure 100. As an example, thesheet members 208 are continuous sheets of a thin metal material. As anon-limiting example, the sheet members 208 are thin sheets of steelfoil (e.g., between approximately 0.016 mm and approximately 0.024 mmthick).

In an example construction, the apparatus 200 may also include one ormore guides 210 (e.g., rollers or other tooling elements) configured tomaintain the orientation of the material layers 112 relative to eachother through one or more zones of the apparatus 200. As an example, theguides 210 may be used to pre-align and/or guide the laminate 110 of thematerial layers 112, and the sheet members 208, to the preheating zone204.

In an example implementation, the pulsating drive mechanism 226 of theapparatus 200 incrementally moves the laminate 110 substantiallycontinuously, in a step-wise manner, through the preheating zone 204 andaway from the material supply zone 202. In an example construction ofthe apparatus 200, the preheating zone 204 includes a preheating device220 (e.g., an oven or furnace). The preheating device 220 may include aplurality of heating elements, or heaters, 222 for example, upperheating elements positioned above the laminate 110 and/or lower heatingelements positioned below the laminate 110.

The preheating device 220 is configured to heat the laminate 110 (e.g.,the stacked laminate of the core 108 sandwiched between the first facesheet 104 and the second face sheet 106 provided from the materialsupply zone 202) to a pre-selected temperature that is sufficiently highto cause softening of the laminate 110 so that is may be subsequentlyformed, for example, to allow preforming of the laminate 110 in apreforming zone 224 and/or thermoforming of the laminate 110 in theconsolidation zone 206 without damaging any of the material layers 112(e.g., the first face sheet 104, the second face sheet 106 and/or thecore 108). As an example, the preheating device 220 heats the laminate110 to a preforming temperature above the glass transition temperatureof the laminate 110 (e.g., the material layers 112) and below or equalto the crystalline melt temperature of the laminate 110 (e.g., thematerial layers 112). In other words, the laminate 110 is heated to apliable preforming temperature by the preheating device 220.

In an example construction, the preheating device 220 is an infrared(IR) convection oven that utilizes short wave electric infrared heaters,medium wave electric infrared heaters, long wave electric infraredheaters or some combination thereof as its heating elements 222. Inanother example construction, the preheating device 220 is a halogenoven or a halogen convection oven that utilizes halogen lamps as itsheating elements 222. In another example construction, the preheatingdevice 220 is a gas fired convection oven. In yet another exampleconstruction, the preheating device 220 is an electric convection oven.

In this example implementation, a preheated laminate 114 (e.g., thestacked laminate of the core 108 sandwiched between the first face sheet104 and the second face sheet 106 after being preheated by thepreheating zone 204) exits the preheating zone 204 and moves into eitherthe preforming zone 224 (FIG. 3) for partial forming, or preforming, ofthe preheated laminate 114 or the consolidation zone 206 (FIG. 2) forconsolidating and final forming of the preheated laminate 114.

FIG. 3 is a schematic illustration of another embodiment of thedisclosed apparatus 200 used to form the composite sandwich structure100. Optionally, the apparatus 200 includes the preforming zone 224. Inanother example implementation, the pulsating drive mechanism 226 of theapparatus 200 incrementally moves the preheated laminate 114substantially continuously, in a step-wise manner, through thepreforming zone 224. In an example construction of the apparatus 200,the preforming zone 224 includes the plurality of heating elements 222and one or more (e.g., a series) of preforming tool dies 228. At leastsome of the preforming tool dies 228 have first and second die halvesthat have a progressive shape. The preforming tool die 228 pre-molds orpre-forms at least a portion of a curvature or feature into thepreheated laminate 114. While only one preforming tool die 228 is shownin FIG. 3, the preforming zone 224 may include any number of preformingtool dies 228. Also, it should be noted here that the preforming tooldies 228 may not be separate from each other, but rather may include asingle die that has multiple separate die shapes formed therein, so thatwith each compression of the preheated laminate 114 by this single die,multiple differing portions of the desired shape are formed.

The number of preforming tool dies 228 or the number of separate dieshapes formed in the preforming tool die 228 may depend upon the desiredshape of the final composite sandwich structure 100. As an example,large shape changes (e.g., large curvatures) may require incremental dieforming utilizing a larger number of preforming tool dies 228 or dieshapes prior to final forming of the composite sandwich structure 100 atthe consolidation zone 206.

In this example implementation, a preformed laminate 116 (e.g., thestacked laminate of the core 108 sandwiched between the first face sheet104 and the second face sheet 106 after being preheated by thepreheating zone 204 and preformed by the preforming zone 224) exits thepreforming zone 224 and moves into the consolidation zone 206 forconsolidating and final forming of the preheated laminate 114.

In an example construction, the preheating operation and the preformingoperation are integrated into a single zone, also generally referred toas the preforming zone 224. Accordingly, in an example construction, thepreheating device 220 and the preforming tool dies 228 are integratedinto the same unit or structure defining the preforming zone 224. Inother words, at least a portion of a curvature or feature is preformedinto the preheated laminate 114 by the preforming tool dies 228 whilethe preformed laminate 116 is within the preheating device 220 and isbeing maintained at the pliable preforming temperature.

Referring to FIGS. 2 and 3, in another example implementation, thepulsating drive mechanism 226 of the apparatus 200 incrementally movesthe preheated laminate 114 (FIG. 2) substantially continuously, in astep-wise manner, through the consolidation zone 206 and away from thepreheating zone 204. Alternatively, the pulsating drive mechanism 226 ofthe apparatus 200 incrementally moves the preformed laminate 116 (FIG.3) substantially continuously, in a step-wise manner, through theconsolidation zone 206 and away from the preforming zone 224.

In an example construction, an output end of the preheating zone 204(FIG. 2) or the preforming zone 224 (FIG. 3) is proximate to (e.g., ator near) or is adjacent to (e.g., next to or adjoining) an input end ofthe consolidation zone 206 so that cooling of the preheated laminate 114(FIG. 2), or preformed laminate 114 (FIG. 3), is minimized or prevented.

In an example construction of the apparatus 200, the consolidation zone206 includes a continuous compression molding device 290. As thepreheated laminate 114 (FIG. 2), or the preformed laminate 116 (FIG. 3),moves forward, it first enters a heating zone 230 of the consolidationzone 206. The heating zone 230 is configured to further heat thepreheated laminate 114, or the preformed laminate 116, to athermoforming temperature above the crystalline melt temperature, forexample, a temperature that is sufficiently high to cause or allow afree flow of the polymeric component of the laminate 110, for example,the polymeric component of the matrix material in the material layers112 (e.g., the first face sheet 104 and/or the second face sheet 106).In an example construction of the apparatus 200, heating zone 230includes at least one heater 234 that heats the preheated laminate 114,or the preformed laminate 116, to the thermoforming, or consolidating,temperature. The heater 234 may include any of various devices suitablefor heating the laminate 110 (e.g., the preheated laminate 114 orpreformed laminate 116), including but not limited to, an oven orinfrared heat lamps.

In this example implementation, a heated laminate 118 (e.g., the stackedlaminate of the core 108 sandwiched between the first face sheet 104 andthe second face sheet 106 after being heated by the heating zone 230)exits the heating zone 230 and moves into a forming zone 232 of theconsolidation zone 206 for consolidating and final forming of the heatedlaminate 118.

In another example implementation, the pulsating drive mechanism 226 ofthe apparatus 200 incrementally moves the heated laminate 118substantially continuously, in a step-wise manner, through the formingzone 232. In an example construction of the apparatus 200, the formingzone 232 includes one or more (e.g., a series) of forming tool dies 236.At least some of the forming tool dies 236 have first and second diehalves that have a progressive shape. The forming tool dies 236 molds orforms at least a portion of a final curvature or feature into the heatedlaminate 118. While only three forming tool dies 236 are shown in FIGS.2 and 3, the forming zone 232 may include any number of forming tooldies 236. Also, it should be noted here that the forming tool dies 236may not be separate from each other, but rather may include a single diethat has multiple separate die shapes formed therein, so that with eachcompression of the heated laminate 118 by this single die, multiplediffering portions of the desired shape are formed.

As the heated laminate 118 moves forward into the forming zone 232, theforming tool dies 236 are brought down, for example, collectively orindividually, at a predefined pressure sufficient to compress andconsolidate (e.g., allow free-flow of the polymeric matrix material) thevarious material layers 12 into the desired shape and/or thickness. Asdescribed above, the layers of the sheet members 208 are positioned overthe outer surfaces of the heated laminate 118 so that the forming tooldies 236 contact sheet members 208, and not the heated laminate 118.

As the forming tool dies 236 are opened, the heated laminate 118 isincrementally advanced within the consolidation zone 206. After which,the forming tool dies 236 are closed again, causing successive sectionsof the heated laminate 118 to be compressed within different temperaturezones, and thereby consolidate the laminate core 108 sandwiched betweenthe first face sheet 104 and the second face sheet 106 in the compressedsection. This process is repeated for each temperature zone of theforming tool dies 236 as the heated laminate 118 is incrementallyadvanced through the consolidation operation (e.g., the consolidationzone 206).

The number of forming tool dies 236 or the number of separate die shapesformed in the forming tool die 236 may depend upon the desired shape ofthe final composite sandwich structure 100. As an example, large shapechanges (e.g., large curvatures) may require incremental die formingutilizing a larger number of forming tool dies 236 or die shapes.

In this example implementation, a consolidated (e.g., fully formed andcompressed) laminate 120 (e.g., the stacked laminate of the core 108sandwiched between the first face sheet 104 and the second face sheet106 after being heated by the heating zone 230 and formed by the formingzone 232) exits the consolidation zone 206.

Any curing process required for the laminate 110 (e.g., thermosetcuring) may occur within the consolidation zone 206, for example, duringconsolidation (e.g., heating and forming) of the laminate 110 (e.g.,within the heating zone 230 and the forming zone 232).

Referring still to FIGS. 2 and 3, in another example implementation, theconsolidated laminate 120 then enters a cooling zone 238 of theconsolidation zone 206, which is separated from the consolidation zone206. In the cooling zone 238, the temperature of the consolidatedlaminate 120 is brought below the free-flowing temperature of the matrixmaterial in the material layers 112, thereby causing the fused orconsolidated laminate 120 to harden to its ultimate pressed shape andform the composite sandwich structure 100. In an example construction,the cooling zone 238 may include, without limitation, active cooling ofthe tooling dies that contact the consolidated laminate 120 or fans orblowers that pass ambient or chilled air over the consolidated laminate120 as it exits the forming zone 232.

In this example implementation, a consolidated and cooled laminate 122(e.g., the stacked laminate of the core 108 sandwiched between the firstface sheet 104 and the second face sheet 106 after being cooled by thecooling zone 238) then exits the consolidation zone 206 where the sheetmembers 208 are removed from the cooled laminate 122 (e.g., thecontinuous length of the composite sandwich structure 100) and taken up,for example, on take-up rolls 240.

In another example implementation, the pulsating drive mechanism 226 ofthe apparatus 200 incrementally moves the composite sandwich structure100 to the cutting zone 212 and away from the consolidation zone 206. Inan example construction of the apparatus 200, the cutting zone 212includes a saw or other cutting tool 242 configured to cut thecontinuous composite sandwich structure 100 to a discrete or finitelength and/or trim away excess material.

In another example implementation, a cut section 124 of the compositesandwich structure 100 then enters the inspection zone 214, which isseparated from the cutting zone 212, where the section 124 of thecomposite sandwich structure 100 is inspected. Inspection of the section124 of the composite sandwich structure 100 may include any visualinspection or other non-destructive inspection or testing operation. Inan example construction, the apparatus 200 may include a materialhandling mechanism 244 (e.g., material rollers) configured to move thecut sections 124 of the composite sandwich structure 100 from thecutting zone 212 to the inspection zone 214.

The final composite sandwich structure 100 may then be removed at theend of the apparatus 200.

FIGS. 4 and 5 graphically illustrates example temperature profiles 150of the laminate 110 as a function of time, which also corresponds to aposition of the laminate 110 as it moves through the apparatus 200.During the preheating operation, the temperature of the laminate 110 isinitially ramped up, at 150A, before reaching and being held at thepreselected preforming temperature 152, at 150B, which may be controlledby the amount of preheating affected within the preheating zone 204 andthe rate at which the laminate 110 passes through the preheating zone204. As illustrated in FIG. 5, if the laminate 110 (e.g., the preheatedlaminate 114) (FIGS. 2 and 3) is subjected to the preforming operation,it remains at the preforming temperature 152, at 150B, as it progressesthrough the sets of preforming tool dies 228 of the preforming zone 224(FIG. 3). During the heating operation, the temperature of the laminate110 (e.g., the preheated laminate 114 or the preformed laminate 116) isfurther ramped up, at 150C, before reaching and being held at thepreselected thermoforming temperature 154, at 150D, which may becontrolled by the amount of heating affected within the heating zone 230and the rate at which the laminate 110 passes through the heating zone230. The laminate 110 (e.g., the heated laminate 118) remains at thethermoforming temperature 154, at 150D, as it progresses through thesets of forming tool dies 236 in the forming zone 232 (FIGS. 2 and 3).The laminate 110 (e.g., the consolidated laminate 120) is then subjectedto a cool down ramp, at 150E, which may be controlled by the amount ofcooling affected within the cooling zone 238 and the rate at which thelaminate 110 passes through the cooling zone 238.

As previously mentioned, the section of the laminate 110 disposed withinthe preforming zone 224 is maintained substantially at the preselectedpreforming temperature 152 during preforming. The section of thelaminate 110 disposed within the forming zone 232 is maintainedsubstantially at the preselected thermoforming temperature 154 duringforming (e.g., compression molding). As illustrated, the thermoformingtemperature 154 is at least as high or higher than the preformingtemperature 152. By maintaining the temperature of the laminate 110above its glass transition and below or equal to its crystalline melttemperature throughout the preheating and optional preforming processand above its crystalline melt temperature through the forming, ormolding, process, including temperature ramp-up and cool down, favorableperformance and/or structural properties of the laminate 110 aremaintained, and are therefore exhibited by the fully formed compositesandwich structure 100.

The processing or operational flow rate of the laminate 110 through theapparatus 200, or the feed rate through each of the zones, is dictatedby the flow rate of the laminate 110 through the consolidation zone 206during the consolidating operation (e.g., the heating and formingoperations). Thus, the preheating zone 204 (FIG. 2), or the preformingzone 224 (FIG. 3), is designed to sufficiently preheat the laminate 110to the preforming temperature 152 during the preheating operation, orthe preforming operation, based on the flow rate of the laminate 110through the consolidation zone 206.

FIG. 6 is a schematic transverse cross-sectional illustration of anembodiment of a tool die 246 of the apparatus 200 used to fabricate thecomposite sandwich structure 100. In this embodiment, the tool dies 246may be examples of the forming tool dies 236 used to form or mold thelaminate 110, for example, the heated laminate 118 during the formingoperation (e.g., in the forming zone 232) to form a substantially flatconsolidated laminate 120 (e.g., the composite sandwich structure 100).

In an example implementation, a substantially flat laminate 110 ispreheated to the preforming temperature during the preheating operation(e.g., in the preheating zone 204) and the preheated laminate 114 isheated to the thermoforming temperature during the heating operation(e.g., in the heating zone 230). Incremental movement of the laminate110 positions a section of the laminate 110 (e.g., a portion or sectionof the heated laminate 118) between an opposing pair of movable tool diehalves 246A and 246B. The die halves 246A, 246B are forced against thelaminate 110 (e.g., the heated laminate 118), as indicated bydirectional force arrows 250, to apply a forming pressure to thelaminate 110. Each of the die halves 246A and 246B has a flat toolsurface 248 thereby forming a substantially flat laminate 110 (e.g.,consolidated laminate 120). To fabricate a substantially flat compositesandwich structure 100, each subsequent tool die 246 (e.g., forming tooldies 236) include die halves 246A and 246B each having a flat toolsurface 248.

FIG. 7 is a schematic transverse cross-sectional illustration of anotherembodiment of the tool die 246 of the apparatus 200 used to fabricatethe composite sandwich structure 100 having a curvature 126. In thisembodiment, the tool dies 246 may be examples of the preforming tooldies 228 used to preform the laminate 110, for example, the preheatedlaminate 114 during the preforming operation (e.g., in the preformingzone 224) to form the preformed laminate 116, or the forming tool dies236 used form or mold the laminate 110, for example, the heated laminate118) during the forming operation (e.g., in the forming zone 232) toform a curved consolidated laminate 120 (e.g., the composite sandwichstructure 100).

In an example implementation, the substantially flat laminate 110 ispreheated to the preforming temperature during the preheating operation(e.g., in the preheating zone 204). Incremental movement of the laminate110 positions a section of the laminate 110 (e.g., a portion or sectionof the preheated laminate 114) between the opposing pair of movable tooldie halves 246A and 246B. The die halves 246A, 246B are forced againstthe laminate 110 (e.g., the preheated laminate 114), as indicated bydirectional force arrows 250, to apply a preforming pressure to thelaminate 110. Each of the die halves 246A and 246B has a curved toolsurface 248 thereby forming a curved laminate 110 (e.g., preformedlaminate 116). As an example, a first die half 146A has a convex-curvedtool surface 248 and a second die half 246B has a concave-curved toolsurface 248. To fabricate the preformed laminate 116 having a curvature,each subsequent tool die 246 (e.g., preforming tool dies 228) includedie halves 246A and 246B each having a curved surface 248. To fabricatethe preformed laminate 116 having a more pronounced curvature, eachsubsequent tool die 246 (e.g., preforming tool dies 228) include diehalves 246A and 246B each having an incrementally sharper curved surface248.

In another example implementation, the substantially flat laminate 110is preheated to the preforming temperature during the preheatingoperation (e.g., in the preheating zone 204), optionally, the laminate(e.g., the preheated laminate 114) is preformed during the preformingoperation (e.g., in the preforming zone 224) and the laminate 110 (e.g.,the preheated laminate 114 or preformed laminate 116) is heated to thethermoforming temperature during the heating operation (e.g., in theheating zone 230). Incremental movement of the laminate 110 positions asection of the laminate 110 (e.g., a portion or section of the heatedlaminate 118) between the opposing pair of movable tool die halves 246Aand 246B. The die halves 246A, 246B are forced against the laminate 110(e.g., the heated laminate 118), as indicated by directional forcearrows 250, to apply the forming pressure to the laminate 110. Each ofthe die halves 246A and 246B has a curved tool surface 248 therebyforming a curved laminate 110 (e.g., consolidated laminate 120). As anexample, a first die half 146A has a convex-curved tool surface 248 anda second die half 246B has a concave-curved tool surface 248. As anotherexample, the first die half 146A has the concave-curved tool surface 248and the second die half 246B has the convex-curved tool surface 248. Tofabricate the consolidated laminate 120 (e.g., the composite sandwichstructure 100) having the curvature 126, each subsequent tool die 246(e.g., forming tool dies 236) include die halves 246A and 246B eachhaving a curved surface 248. To fabricate the consolidated laminate 120(e.g., the composite sandwich structure 100) having a more pronouncedcurvature 126, each subsequent tool die 246 (e.g., forming tool dies236) include die halves 246A and 246B each having an incrementallysharper curved surface 248.

FIG. 8 is a schematic transverse cross-sectional illustration of anotherembodiment of the tool die 246 of the apparatus 200 used to fabricatethe composite sandwich structure 100 having one or more surface features128. In this embodiment, the tool dies 246 may be examples of theforming tool dies 236 used to form or mold the laminate 110, forexample, the heated laminate 118 during the forming operation (e.g., inthe forming zone 232) to form a consolidated laminate 120 (e.g., thecomposite sandwich structure 100) having the surface feature 128 formedtherein.

In an example implementation, the substantially flat laminate 110 ispreheated to the preforming temperature during the preheating operation(e.g., in the preheating zone 204), optionally, the laminate (e.g., thepreheated laminate 114) is preformed during the preforming operation(e.g., in the preforming zone 224) and the laminate 110 (e.g., thepreheated laminate 114 or preformed laminate 116) is heated to thethermoforming temperature during the heating operation (e.g., in theheating zone 230). Incremental movement of the laminate 110 positions asection of the laminate 110 (e.g., a portion or section of the heatedlaminate 118) between the opposing pair of movable tool die halves 246Aand 246B. The die halves 246A, 246B are forced against the laminate 110(e.g., the heated laminate 118), as indicated by directional forcearrows 250, to apply the forming pressure to the laminate 110. Each ofthe die halves 246A and 246B has a protrusion 252 extending from thetool surface 248 thereby forming a laminate 110 (e.g., consolidatedlaminate 120) having the surface feature 128. As an example, the firstdie half 146A has a substantially flat or curved tool surface 248 andthe second die half 246B has a substantially flat or curved tool surface248 corresponding to the shape of the tool surface 248 of the first diehalf 246A and one or more protrusions 252. To fabricate the consolidatedlaminate 120 (e.g., the composite sandwich structure 100) having thesurface feature 128, one of the die halves 246A and 246B of eachsubsequent tool die 246 (e.g., forming tool dies 236) includes theprotrusion 252. To fabricate the consolidated laminate 120 (e.g., thecomposite sandwich structure 100) having a more pronounced surfacefeature 128, one of the die halves 246A and 246B of each subsequent tooldie 246 (e.g., forming tool dies 236) includes an incrementally largerprotrusion 252.

In another example embodiment, the disclosed apparatus 200 may includeat least one of a texturing zone 254 and/or a coating zone 260 or acombination of the texturing zone 254 and the coating zone 260 (e.g., acoating-texturing zone 266 or a texturing-coating zone 272) to apply atleast one of a surface texture 132 and/or a surface coating 136 to atleast one surface of the composite sandwich structure 100 in acontinuous process. As will become clear to one skilled in the art,depending on the texturing process and/or coating process used, theorder in which the surface texture 132 and/or the surface coating 136 isapplied to at least one surface of the composite sandwich structure 100may vary (e.g., the sequential, or in-line, order of the texturing zone254 and/or the coating zone 260).

FIG. 9 is a schematic illustration of another embodiment of thedisclosed apparatus 200 used to form the composite sandwich structure100. In this embodiment, the apparatus 200 also includes the texturingzone (e.g., a texture-stamping zone) 254. In an example implementation,the pulsating drive mechanism 226 incrementally moves the consolidatedlaminate 120 substantially continuously, in a step-wise manner, throughthe texturing zone 254 and away from the consolidation zone 206 (e.g.,the forming zone 232). In an example construction of the apparatus 200,the texturing zone 254 includes a texturing device 292 that includes oneor more texture-stamping tool dies 256. At least some of thetexture-stamping tool dies 256 have first and second die halves thathave a textured tool surface 258. In an example construction, thetextured tool surface 258 is integral to the texture-stamping tool dies256. In another example construction, the textured tool surface 258 takethe form of removable inserts coupled to the texture-stamping tool dies256. The texture-stamping tool dies 256 stamps, forms or otherwiseimparts a surface texture 132 into at least one surface of the laminate110 (e.g., the consolidated laminate 120).

In an example construction, an output end of the consolidation zone 206(e.g., the forming zone 232) is proximate to (e.g., at or near) or isadjacent to (e.g., next to or adjoining) an input end of the texturingzone 254 so that cooling of the consolidated laminate 120 is minimized.In other words, after exiting the consolidation zone 206, the laminate110 (e.g., the consolidated laminate 120) is maintained at a temperaturesufficiently high to impart the surface texture 132 to at least onesurface of the laminate 110 (e.g., the consolidated laminate 120).

As the consolidated laminate 120 moves forward into the texturing zone254, the texture-stamping tool dies 256 are brought down, for example,collectively or individually, at a predefined pressure sufficient toimpart the surface texture 132 into the consolidated laminate 120.

In the illustrated embodiment, the sheet members 208 are removed fromthe outer surfaces of the laminate 110 (e.g., the consolidated laminate120) before the texturing (e.g., texture-stamping) operation (e.g.,entering the texturing zone 254) so that the texture-stamping tool dies256 make direct contact with the outer surface of the laminate 110(e.g., the consolidated laminate 120) to impart the surface texture 132.However, in other example implementations, the sheet members 208 may beremoved from the outer surfaces of the laminate 110 (e.g., theconsolidated laminate 120) after the texture-stamping operation (e.g.,entering the texturing zone 254) so that the texture-stamping tool dies256 make direct contact with the sheet member 208 to impart the surfacetexture 132 the outer surface of the laminate 110 (e.g., theconsolidated laminate 120) through the sheet member 208.

In the illustrated embodiment, the pulsating drive mechanism 226 islocated after the texturing zone 254. However, in other exampleconstructions of the apparatus 200, the pulsating drive mechanism 226may be positioned at other locations along the apparatus 200.

In the illustrated embodiment, a textured laminate 130 enters thecooling zone 238, for example, located after the texturing zone 254,where the temperature of the textured laminate 130 is brought below thefree-flowing temperature of the matrix material in the material layers112, thereby causing the consolidated and textured laminate 130 toharden to its ultimate shape and form the composite sandwich structure100 having the desired surface texture 132.

FIG. 10 is a schematic illustration of another embodiment of thedisclosed apparatus 200 used to form the composite sandwich structure100. In this embodiment, the apparatus 200 also includes a coating zone260. In an example implementation, the pulsating drive mechanism 226incrementally moves the laminate 110 (e.g., the textured laminate 130)substantially continuously, in a step-wise manner, through the coatingzone 260. In another example implementation, the apparatus 200 may notinclude the texturing zone 254 (not shown). In this embodiment, thepulsating drive mechanism 226 incrementally moves the laminate 110(e.g., the cooled laminate 122) substantially continuously, in astep-wise manner, through the coating zone 260. In an exampleconstruction of the apparatus 200, the coating zone 260 includes acoating device 294 that includes one or more applicators 262. Theapplicator 262 is configured to impart a surface coating 136 onto atleast one surface of the laminate 110 (e.g., the consolidated,optionally textured, and cooled laminate) to form a coated laminate 134.In an example, the applicator 262 is a sprayer configured to apply aliquid coating 264 such as, and without limitation, paint (e.g., acolored paint, an ultraviolet (UV) paint, etc.), a gloss coating, ametallic surface-finish coating, a protective coating and the like, toat least one surface of the laminate 110. In other examples (not shown),the applicator 262 may include other types of mechanisms for applyingthe coating 264 such as brushes, rollers and the like.

While the illustrated embodiment shows the applicator 262 applying thecoating 264 to only one surface of the laminate 110, additionalapplicators 262 may be used to apply coating 264 to both surfaces of thelaminate 110 so that both surfaces of the laminate 110 (e.g., thetextured and coated laminate) include the surface texture 132 and thesurface coating 136.

In an example construction, an input end of the coating zone 260 isspaced away from an output end of the texturing zone 254 so that thelaminate 110 (e.g., the consolidated and textured laminate) cools beforeapplication of the coating 264. In an example implementation, and asillustrated, the textured laminate 130 enters the cooling zone 238, forexample, located between the texturing zone 254 and the coating zone260, where the temperature of the textured laminate 130 is reducedbefore the coating operation.

FIG. 11 is a schematic illustration of another embodiment of thedisclosed apparatus 200 used to form the composite sandwich structure100. In this embodiment, the apparatus 200 also includes acoating-texturing zone 266. In an example implementation, the pulsatingdrive mechanism 226 incrementally moves the laminate 110 (e.g., theconsolidated and cooled laminate) substantially continuously, in astep-wise manner, through the coating-texturing zone 266. In an exampleconstruction of the apparatus 200, the coating-texturing zone 266includes the coating device 294 that includes one or more applicators262. The applicator 262 is configured to impart the surface coating 136onto at least one surface of the laminate 110 (e.g., the consolidatedand cooled laminate). In an example, the applicator 262 is a sprayerconfigured to apply liquid coating 264 (e.g., a gelcoat) to the surfaceof the laminate 110. In other examples, the applicator 262 may includeother types of mechanisms for applying the coating 264 such as brushes,rollers and the like. The coating-texturing zone 266 also includes thetexturing device 292 that includes one or more (e.g., a series) oftextured rollers 268 having a textured surface 270 configured to impartthe surface texture 132. In an example implementation, the texturedrollers 268 are placed into contact with the coated surface of thelaminate 110 so that the textured surface 270 of the textured roller 268forms or otherwise imparts the surface texture 132 into the coating 264(e.g., the surface coating 136) as it cures, for example, by a thermalor UV curing process.

While the illustrated embodiment shows the applicator 262 applying thecoating 264 and the textured rollers 268 texturizing the coating 264 ononly one surface of the laminate 110, additional applicators 262 andtextured rollers 268 may be used to apply and texturize the coating 264to both surfaces of the laminate 110 so that both surfaces of thelaminate 110 (e.g., the coated-textured laminate 138) include thesurface coating 136 and the surface texture 132.

FIG. 12 is a schematic illustration of another embodiment of thedisclosed apparatus 200 used to form the composite sandwich structure100. In this embodiment, the apparatus 200 also includes atexturing-coating zone 272. In an example implementation, the pulsatingdrive mechanism 226 incrementally moves the laminate 110 (e.g., theconsolidated and cooled laminate) substantially continuously, in astep-wise manner, through the texturing-coating zone 272. In an exampleconstruction of the apparatus 200, the texturing-coating zone 272includes the texturing device 292 that includes a film applicator 278configured to apply a thin film 274 to at least one surface of thelaminate 110 (e.g., the consolidated and cooled laminate). As anexample, the film 274 is supplied in continuous form, for example, froma supply reel 276. The texturing-coating zone 272 also includes one ormore (e.g., a series) of textured rollers 268 having a textured surface270 configured to impart the surface texture 132 to the thin film 274.In an example implementation, the textured rollers 268 are placed intocontact with the thin film 274 applied to the surface of the laminate110 so that the textured surface 270 of the textured roller 268 forms orotherwise imparts the surface texture 132 into the film 274. In thisexample, the textured rollers 268 may be heated to a temperaturesufficient to heat apply the thin film 274. The film 274 may alsoinclude at least one of a color (e.g., at least one color or a pluralityof colors) and/or a finish (e.g., a glossy finish, a matte finish, ametallic finish, a protective finish, etc.) so that the film 274 alsoimparts the surface coating 136 to the laminate 110 (e.g., the texturedand coated laminate).

While the illustrated embodiment shows the film applicator 278 applyingthe film 274 and the textured rollers 268 texturizing the film 274 ononly one surface of the laminate 110, additional film applicators 278and textured rollers 268 may be used to apply and texturize the film 274to both surfaces of the laminate 110 so that both surfaces of thelaminate 110 (e.g., the coated-textured laminate 138) include thesurface texture 132, and, optionally, the surface coating 136 (e.g.,coloring).

FIG. 13 is a schematic illustration of another embodiment of thedisclosed apparatus 200 used to form the composite sandwich structure100. In this embodiment, the apparatus 200 also includes thetexturing-coating zone 272. In an example implementation, the pulsatingdrive mechanism 226 incrementally moves the laminate 110 (e.g., theconsolidated and cooled laminate) substantially continuously, in astep-wise manner, through the texturing-coating zone 272. In an exampleconstruction of the apparatus 200, the texturing-coating zone 272includes the texturing device 292 that includes the film applicator 278configured to apply a textured film 280 to at least one surface of thelaminate 110 (e.g., the consolidated and cooled laminate). As anexample, the textured film 280 includes a thin film with a textured foilor other texture preformed into the thin film. As an example, thetextured film 280 is supplied in continuous form, for example, from asupply reel 282. The texturing-coating zone 272 also includes one ormore (e.g., a series) of consolidation rollers 284 configured toconsolidate the textured film 280 and the laminate 110. In an exampleimplementation, the consolidation rollers 284 are placed into contactwith the textured film 280 applied to the surface of the laminate 110 toimpart the surface texture 132 into the surface of the laminate 110. Inthis example, the consolidation rollers 284 may be heated to atemperature sufficient to heat apply the textured film 280. The texturedfilm 280 may also include at least one of a color (e.g., at least onecolor or a plurality of colors) and/or a finish (e.g., a glossy finish,a matte finish, a metallic finish, a protective finish, etc.) so thatthe textured film 280 also imparts the surface coating 136 (e.g., thesurface color) to the laminate 110 (e.g., the textured and coated orcolored laminate).

While the illustrated embodiment shows the film applicator 278 applyingthe textured film 280 and the consolidation rollers 284 consolidatingthe textured film 280 on only one surface of the laminate 110,additional film applicators 278 and consolidation rollers 284 may beused to apply and consolidate the textured film 280 to both surfaces ofthe laminate 110 so that both surfaces of the laminate 110 (e.g., thecoated-textured laminate 138) include the surface texture 132, and,optionally, the surface coating 136 (e.g., coloring).

FIG. 14 is a schematic illustration of another embodiment of thedisclosed apparatus 200 used to form the composite sandwich structure100. In this embodiment, the apparatus 200 also includes thecoating-texturing zone 266. In an example implementation, the pulsatingdrive mechanism 226 incrementally moves the laminate 110 (e.g., theconsolidated and cooled laminate) substantially continuously, in astep-wise manner, through the coating-texturing zone 266. In an exampleconstruction of the apparatus 200, the coating-texturing zone 266includes the coating device 294 that includes one or more printers 286.The printer 286 is configured to apply a printable material 288 andimpart the surface coating 136 (e.g., coloring), and, optionally, thesurface texture 132, onto at least one surface of the laminate 110(e.g., the consolidated and cooled laminate). In an example, the printer286 is an ink jet printer configured to apply ink to the surface of thelaminate 110 to form the surface coating 136 (e.g., coloring). Inanother example, the printer 286 is a 3D printer configured to applysuccessive layers of material (e.g., an extruded thermoplastic material)to the surface of the laminate 110 to form the surface texture 132and/or the surface coating 136 (e.g., coloring).

While the illustrated embodiment shows the printer 286 applying theprintable material 288 on only one surface of the laminate 110,additional printers 286 may be used to apply, and, optionally,texturize, the printable material 288 to both surfaces of the laminate110 so that both surfaces of the laminate 110 (e.g., the coated-texturedlaminate 138) include the surface coating 136, and, optionally, thesurface texture 132.

FIG. 15 is a flow diagram of an example embodiment of the disclosedmethod 300 for continuously fabricating the composite sandwich structure100. Beginning at block 302, a stacked laminate 110 of material layers112 (e.g., the first face sheet 104, the second face sheet 106 and thecore 108 sandwiched between the first face sheet 104 and the second facesheet 106) is formed. As an example, the laminate 110 may bepre-constructed as a stacked and tacked laminate introduced to thematerial supply zone 202. As another example, the laminate 110 may be alayup formed by aligning the material layers 112 at the material supplyzone 202.

As shown at block 304, the laminate 110 is substantially continuouslymoved through the preheating zone 204 where, at block 306, the laminate110 is preheated to the preforming temperature 152 above the glasstransition temperature of the laminate 110 and below or equal to thecrystalline melt temperature of the laminate 110 as the laminate 110 isbeing moved through the preheating zone 204. Preheating (block 306) thelaminate 110 may be performed using the preheating device 220, asdescribed above.

Optionally, as shown at block 308, the laminate 110 (e.g., the preheatedlaminate 114) is substantially continuously moved through the preformingzone 224 where, at block 310, the laminate 110 is incrementallypreformed at the preforming temperature 152 into the partially desiredshape as the laminate 110 is being moved through the preforming zone224. Preforming (block 310) the laminate 110 may be performed by thepreforming tool dies 228, as described above.

As shown at block 312, the laminate 110 (e.g., the preheated laminate114 or the preformed laminate 116) is substantially continuously movedthrough the consolidation zone 206 where, at block 314, the laminate 110is consolidated as the laminate 110 is being moved through theconsolidation zone 206 to form the continuous length of the compositesandwich structure 100. As described above, consolidating (block 314)the laminate 110 includes heating the laminate 110 to a thermoformingtemperature 154 above the crystalline melt temperature of the laminate100 (e.g., sufficient to allow the free flow of the polymeric componentof the laminate 110) as the laminate 110 is being moved through theheating zone 230 of the consolidation zone 206 and incrementally formingthe laminate 110 at the thermoforming temperature 154 into the desiredshape (e.g., having the curvature 126 and/or surface feature 128) as thelaminate is being moved through the forming zone 232 of theconsolidation zone 206. Consolidating (block 314) the laminate 110 maybe performed using the continuous compression molding device 290 (e.g.,the heater 234 and the forming tool dies 236), as described above.

Optionally, as shown at block 316, the composite sandwich structure 100is substantially continuously moved through at least one of thetexturing zone 254 and/or the coating zone 260 where, at block 318, atleast one of the surface texture 132 and/or the surface coating 136 isapplied to at least one surface of the composite sandwich structure 100.Applying (block 318) at least one of the surface texture 132 and/or thesurface coating 136 may be performed by a respective one of thetexturing device 292 and/or the coating device 294, as described above.

As shown at block 320, the laminate 110 (e.g., the consolidated laminate120) is cooled. As shown at block 322, the continuous length of thecomposite sandwich structure 100 is cut into finite lengths of thecomposite sandwich structure 100. As shown at block 324, the finitelengths of the composite sandwich structure 100 are inspected.

In an example implementation, moving (block 302) the laminate 110,substantially continuously, through the preheating zone 204 and moving(block 312) the laminate 110, substantially continuously, through theconsolidation zone 206 is performed along a linear path. Similarly,moving (block 308) the laminate 110, substantially continuously, throughthe preforming zone 224 is performed along a linear path. Further,moving (block 316) the composite sandwich structure 100 through at leastone of the texturing zone 254 and/or the coating zone 260 is performedalong a linear path.

The various zones (e.g., the material supply zone 202, the preheatingzone 204, the preforming zone 224, the consolidation zone 206, thecooling zone 238, the texturing zone 254, coating zone 260 and thecutting zone 212), and the devices associated with each respective zone,of the disclosed apparatus 200 are arranged in a continuous linkedsequence, for example, side-by-side and in line with one another.Similarly, the operations of the fabrication process of the disclosedcomposite sandwich structure 100 (e.g., method 300) may be performed inincremental progressive steps in a continuous linked sequence. In anexample implementation, preheating (block 306) the laminate 110 isperformed in incremental progressive steps (e.g., in a stepwise mannerprogressing in incremental or sequentially adjacent steps a section at atime) as the laminate 110 is moved substantially continuously throughthe preheating zone 204 and consolidating (block 314) the laminate 110is performed in incremental progressive steps (e.g., in a stepwisemanner progressing in incremental or sequentially adjacent steps asection at a time) as the laminate 110 is moved substantiallycontinuously through the consolidation zone 206 204. Similarly,preforming (block 310) the laminate is performed in incrementalprogressive steps (e.g., in a stepwise manner progressing in incrementalor sequentially adjacent steps a section at a time) as the laminate 110is moved substantially continuously through the preforming zone 224.Further, applying (block 318) at least one of the surface texture 132and/or the surface coating 136 is performed in incremental progressivesteps (e.g., in a stepwise manner progressing in incremental orsequentially adjacent steps a section at a time) as the laminate 110 ismoved substantially continuously through the texturing zone 254 and/orthe coating zone 260.

Embodiments of the continuously formed composite sandwich structure 100and apparatus 200 and method 300 for continuously fabricating thecomposite sandwich structure 100 disclosed herein may find use in avariety of potential applications, particularly in the transportationindustry, including for example, aerospace, marine and automotiveapplications. Thus, referring now to FIGS. 16 and 17, embodiments of thecontinuously formed composite sandwich structure 100 and apparatus 200and method 300 for continuously fabricating the composite sandwichstructure 100 may be used in the context of an aircraft manufacturingand service method 1100, as shown in FIG. 16, and an aircraft 1200, asshown in FIG. 17. Aircraft applications of the disclosed embodiments mayinclude interior panels, for example, and without limitation, sandwichpanels used for flooring, ceilings, sidewalls, lavatories, stow bins,cargo hold liners and other interior aircraft structures.

During pre-production, the illustrative method 1100 may includespecification and design, as shown at block 1102, of aircraft 1200 andmaterial procurement, as shown at block 1104. During production,component and subassembly manufacturing, as shown at block 1106, andsystem integration, as shown at block 1108, of the aircraft 1200 maytake place. Production of the continuously formed composite sandwichstructure 100, as described herein, may be accomplished as a portion ofthe production, component and subassembly manufacturing step (block1106) and/or as a portion of the system integration (block 1108).Thereafter, the aircraft 1200 may go through certification and delivery,as shown block 1110, to be placed in service, as shown at block 1112.While in service, the aircraft 1200 may be scheduled for routinemaintenance and service, as shown at block 1114. Routine maintenance andservice may include modification, reconfiguration, refurbishment, etc.of one or more systems of the aircraft 1200.

Each of the processes of illustrative method 1100 may be performed orcarried out by a system integrator, a third party, and/or an operator(e.g., a customer). For the purposes of this description, a systemintegrator may include, without limitation, any number of aircraftmanufacturers and major-system subcontractors; a third party mayinclude, without limitation, any number of vendors, subcontractors, andsuppliers; and an operator may be an airline, leasing company, militaryentity, service organization, and so on.

As shown in FIG. 17, the aircraft 1200 produced by the illustrativemethod 1100 may include an airframe 1202, for example, having compositesandwich panels or other composite sandwich structures 100 continuouslyfabricated using the apparatus 200 and method 300, a plurality ofhigh-level systems 1204 and an interior 1206. Examples of the high-levelsystems 1204 include one or more of a propulsion system 1208, anelectrical system 1210, a hydraulic system 1212 and an environmentalsystem 1214. Any number of other systems may be included. Although anaerospace example is shown, the principles disclosed herein may beapplied to other industries, such as the automotive industry, the marineindustry, and the like.

The systems, apparatus and methods shown or described herein may beemployed during any one or more of the stages of the manufacturing andservice method 1100. For example, components or subassembliescorresponding to component and subassembly manufacturing (block 1106)may be fabricated or manufactured in a manner similar to components orsubassemblies produced while the aircraft 1200 is in service (block1112). Also, one or more examples of the systems, apparatus, andmethods, or combination thereof may be utilized during production stages(blocks 1108 and 1110). Similarly, one or more examples of the systems,apparatus, and methods, or a combination thereof, may be utilized, forexample and without limitation, while the aircraft 1200 is in service(block 1112) and during maintenance and service stage (block 1114).

Reference herein to “embodiment” means that one or more feature,structure, element, component or characteristic described in connectionwith the embodiment is included in at least one implementation of thedisclosed invention. Thus, the phrase “one embodiment,” “anotherembodiment,” and similar language throughout the present disclosure may,but do not necessarily, refer to the same embodiment. Further, thesubject matter characterizing any one embodiment may, but does notnecessarily, include the subject matter characterizing any otherembodiment.

Similarly, reference herein to “example” means that one or more feature,structure, element, component or characteristic described in connectionwith the example is included in at least one embodiment. Thus, thephrases “one example,” “another example,” and similar languagethroughout the present disclosure may, but do not necessarily, refer tothe same example. Further, the subject matter characterizing any oneexample may, but does not necessarily, include the subject mattercharacterizing any other example.

Unless otherwise indicated, the terms “first,” “second,” etc. are usedherein merely as labels, and are not intended to impose ordinal,positional, or hierarchical requirements on the items to which theseterms refer. Moreover, reference to a “second” item does not require orpreclude the existence of lower-numbered item (e.g., a “first” item)and/or a higher-numbered item (e.g., a “third” item).

As used herein, the phrase “at least one of”, when used with a list ofitems, means different combinations of one or more of the listed itemsmay be used and only one of the items in the list may be needed. Theitem may be a particular object, thing, or category. In other words, “atleast one of” means any combination of items or number of items may beused from the list, but not all of the items in the list may berequired. For example, “at least one of item A, item B, and item C” maymean item A; item A and item B; item B; item A, item B, and item C; oritem B and item C. In some cases, “at least one of item A, item B, anditem C” may mean, for example and without limitation, two of item A, oneof item B, and ten of item C; four of item B and seven of item C; orsome other suitable combination.

As used herein, the terms “approximately” and “about” represent anamount close to the stated amount that still performs the desiredfunction or achieves the desired result. For example, the terms“approximately” and “about” may refer to an amount that is within lessthan 10% of, within less than 5% of, within less than 1% of, within lessthan 0.1% of, and within less than 0.01% of the stated amount.

As used herein, the term “substantially” may include exactly andsimilar, which is to an extent that it may be perceived as being exact.For illustration purposes only and not as a limiting example, the term“substantially” may be quantified as a variance of ±5% from the exact oractual. For example, the phrase “A is substantially the same as B” mayencompass embodiments where A is exactly the same as B, or where A maybe within a variance of ±5%, for example of a value, of B, or viceversa.

As used herein, the terms “partially” or “at least a portion of” mayrepresent an amount of a whole that includes an amount of the whole thatmay include the whole. For example, the term “a portion of” may refer toan amount that is greater than 0.01% of, greater than 0.1% of, greaterthan 1% of, greater than 10% of, greater than 20% of, greater than 30%of, greater than 40% of, greater than 50% of, greater than 60%, greaterthan 70% of, greater than 80% of, greater than 90% of, greater than 95%of, greater than 99% of, and 100% of the whole.

In FIG. 17, referred to above, solid lines, if any, connecting variouselements and/or components represent mechanical, electrical, fluid,optical, electromagnetic and other couplings and/or combinationsthereof. As used herein, “coupled” means associated directly as well asindirectly. For example, a member A may be directly associated with amember B, or may be indirectly associated therewith, e.g., via anothermember C. It will be understood that not all relationships among thevarious disclosed elements are necessarily represented. Accordingly,couplings other than those depicted in the block diagrams may alsoexist. Dashed lines, if any, connecting blocks designating the variouselements and/or components represent couplings similar in function andpurpose to those represented by solid lines; however, couplingsrepresented by the dashed lines are either selectively provided orrelate to alternative examples of the present disclosure. Likewise,elements and/or components, if any, represented with dashed lines,indicate alternative examples of the present disclosure. One or moreelements shown in solid and/or dashed lines may be omitted from aparticular example without departing from the scope of the presentdisclosure. Environmental elements, if any, are represented with dottedlines. Virtual (imaginary) elements may also be shown for clarity. Thoseskilled in the art will appreciate that some of the features illustratedin FIG. 17 may be combined in various ways without the need to includeother features described in FIG. 17, other drawing figures, and/or theaccompanying disclosure, even though such combination or combinationsare not explicitly illustrated herein. Similarly, additional featuresnot limited to the examples presented, may be combined with some or allof the features shown and described herein.

In FIGS. 15 and 16, referred to above, the blocks may representoperations and/or portions thereof and lines connecting the variousblocks do not imply any particular order or dependency of the operationsor portions thereof. Blocks, if any, represented by dashed linesindicate alternative operations and/or portions thereof. Dashed lines,if any, connecting the various blocks represent alternative dependenciesof the operations or portions thereof. It will be understood that notall dependencies among the various disclosed operations are necessarilyrepresented. FIGS. 15 and 16 and the accompanying disclosure describingthe operations of the disclosed methods set forth herein should not beinterpreted as necessarily determining a sequence in which theoperations are to be performed. Rather, although one illustrative orderis indicated, it is to be understood that the sequence of the operationsmay be modified when appropriate. Accordingly, modifications, additionsand/or omissions may be made to the operations illustrated and certainoperations may be performed in a different order or simultaneously.Additionally, those skilled in the art will appreciate that not alloperations described need be performed.

Although various embodiments of the disclosed apparatus, systems andmethods have been shown and described, modifications may occur to thoseskilled in the art upon reading the specification. The presentapplication includes such modifications and is limited only by the scopeof the claims.

What is claimed is:
 1. A method for continuously fabricating a compositesandwich structure, said method comprising: preheating a laminate to apreforming temperature above a glass transition temperature of saidlaminate but below or equal to a crystalline melt temperature of saidlaminate as said laminate is substantially continuously moved through apreheating zone, wherein said laminate comprises a first face sheet, asecond face sheet and a core sandwiched between said first face sheetand said second face sheet; consolidating said laminate as said laminateis substantially continuously moved through a consolidation zonearranged in a continuous linked sequence with said preheating zone toform a continuous length of said composite sandwich structure; movingsaid composite sandwich structure, substantially continuously, throughat least one of a texturing zone and a coating zone; and incrementallyapplying at least one of a surface texture and a surface coating to atleast one surface of said composite sandwich structure.
 2. The method ofclaim 1 wherein consolidating said laminate comprises: heating saidlaminate to a thermoforming temperature above said crystalline melttemperature of said laminate as said laminate is being moved through aheating zone of said consolidation zone; and incrementally forming saidlaminate at said thermoforming temperature into a desired shape as saidlaminate is being moved through a forming zone of said consolidationzone.
 3. The method of claim 2 further comprising incrementallypreforming said laminate at said preforming temperature into a partiallydesired shape as said laminate is substantially continuously movedthrough preforming zone arranged in said continuous linked sequencebetween said preheating zone and said consolidation zone.
 4. The methodof claim 1 wherein incrementally applying said surface texture comprisestexture-stamping said surface texture into said at least one surface ofsaid composite sandwich structure as said composite sandwich structureis being moved through said texturing zone.
 5. The method of claim 4wherein incrementally applying said surface texture is performed at atemperature sufficiently high to allow a textured surface of at leastone of texture-stamping tool dies to stamp said surface texture intosaid at least one surface of said composite sandwich structure as saidcomposite sandwich structure is being moved through said texturing zone.6. The method of claim 5 wherein incrementally applying said surfacecoating comprises applying a liquid coating onto said at least onesurface of said composite sandwich structure over said surface textureas said composite sandwich structure is being moved through said coatingzone.
 7. The method of claim 1 wherein incrementally applying saidsurface coating comprises applying a liquid coating onto said at leastone surface of said composite sandwich structure as said compositesandwich structure is being moved through said coating zone.
 8. Themethod of claim 7 wherein incrementally applying said surface texturecomprises imprinting said surface texture into said liquid coating assaid composite sandwich structure is being moved through said texturingzone.
 9. The method of claim 1 wherein incrementally applying saidsurface texture comprises applying a thin film onto said at least onesurface of said composite sandwich structure and at least one texturedroller to imprint said surface texture into said thin film as saidcomposite sandwich structure is being moved through said texturing zone.10. The method of claim 9 wherein said thin film comprises at least oneof a color and a finish.
 11. The method of claim 1 wherein incrementallyapplying said surface texture comprises applying a textured film ontosaid at least one surface of said composite sandwich structure and atleast one consolidation roller to consolidate said textured film andsaid at least one surface of said composite sandwich structure as saidcomposite sandwich structure is being moved through said texturing zone.12. The method of claim 11 wherein said textured film comprises at leastone of a color and a finish.
 13. The method of claim 1 whereinincrementally applying said surface coating comprises applying one ofpaint and ink onto said at least one surface of said composite sandwichstructure as said composite sandwich structure is being moved throughsaid coating zone.
 14. An apparatus for continuously fabricating acomposite sandwich structure, said apparatus comprising: a preheatingdevice to preheat a laminate to a preforming temperature above a glasstransition temperature of said laminate but below or equal to acrystalline melt temperature of said laminate as said laminate is moved,substantially continuously, through said preheating device, wherein saidlaminate comprises a first face sheet, a second face sheet and a coresandwiched between said first face sheet and said second face sheet; acontinuous compression molding device to consolidate said laminate assaid laminate is moved, substantially continuously, through saidcontinuous compression molding device to form a continuous length ofsaid composite sandwich structure; and at least one of a texturingdevice and a coating device to apply at least one of a surface textureand a surface coating to at least one surface of said composite sandwichstructure; and wherein said preheating device, said continuouscompression molding device and said at least one of said texturingdevice and said coating device are arranged in a continuous linkedsequence.
 15. The apparatus of claim 14 wherein: said texturing devicecomprises at least one set of texture-stamping tool dies to stamp saidsurface texture into said at least one surface of said compositesandwich structure as said composite sandwich structure is being movedthrough said texturing device, and said coating device comprises anapplicator to apply a liquid coating onto said at least one surface ofsaid composite sandwich structure as said composite sandwich structureis being moved through said coating device.
 16. The apparatus of claim14 wherein: said coating device comprises an applicator to apply aliquid coating onto said at least one surface of said composite sandwichstructure as said composite sandwich structure is being moved throughsaid coating device; and said texturing device comprises at least onetextured roller to imprint said surface texture into said liquid coatingas said composite sandwich structure is being moved through saidtexturing device.
 17. The apparatus of claim 14 wherein: said texturingdevice comprises a film applicator to apply a thin film onto said atleast one surface of said composite sandwich structure and at least onetextured roller to imprint said surface texture into said thin film assaid composite sandwich structure is being moved through said texturingdevice, and said thin film comprises at least one of a color and afinish.
 18. The apparatus of claim 14 wherein: said texturing devicecomprises a film applicator to apply a textured film onto said at leastone surface of said composite sandwich structure and at least oneconsolidation roller to consolidate said textured film and said at leastone surface of said composite sandwich structure as said compositesandwich structure is being moved through said texturing device, andtextured film comprises at least one of a color and a finish.
 19. Theapparatus of claim 14 wherein said coating device comprises a printer toapply a printable material onto said at least one surface of saidcomposite sandwich structure as said composite sandwich structure isbeing moved through said coating device.
 20. A continuously fabricatedcomposite sandwich structure comprising: a laminate comprising a firstface sheet, a second face sheet and a core sandwiched between said firstface sheet and said second face sheet; and at least one of a surfacetexture and a surface coating applied to said composite sandwichstructure; and wherein said composite sandwich structure is continuouslyfabricated by: preheating said laminate to a preforming temperatureabove a glass transition temperature of said laminate but below or equalto a crystalline melt temperature of said laminate as said laminate issubstantially continuously moved through a preheating zone;consolidating said laminate by heating said laminate to a thermoformingtemperature sufficient to allow a free flow of a polymeric component ofsaid laminate and incrementally forming said laminate at saidthermoforming temperature into a desired shape as said laminate issubstantially continuously moved through a consolidation zone arrangedin a continuous linked sequence with said preheating zone to form acontinuous length of said composite sandwich structure; andincrementally applying at least one of said surface texture and saidsurface coating to said at least one surface of said composite sandwichstructure as said composite sandwich structure is substantiallycontinuously moved through at least one of a texturing zone and acoating zone arranged in said continuous linked sequence with saidconsolidation zone.